| -- | -- | -- | TUFNOL |
| -- | -- | Hgw 2082.5 | (D) DIN 7735 |
| -- | -- | PF CC 202 | EN 60893 / IEC 893 |
| -- | -- | 2572-F4 | GB) BS |
| -- | -- | CE | USA) NEMA L1 |
| -- | -- | 150 C | F) NF C26 |
| -- | -- | S-PF-CC 2 | CH) VSM |
| -- | -- | phenol | Resin |
| -- | -- | cotton fabric | Reinforcement |
| -- | -- | med. weave | |
| Density | DIN53479 | 1,3 -1,4 | g/cm |
| Flexural strength, unproces./ 23º C | DIN 53452 | 115 | MPa |
| lmpact strength an 10 and a n 15 | DIN53453 | 20 | kJ/m |
| Notched bar impact value a k 10 | DIN 53453 | 10 | kJ/m |
| Notched bar impact value a k 15 | DIN 53453 | 15 | kJ/m |
| Tensile strength SB | DIN 53455 | 60 | MPa |
| Compressive strength ódB | DIN 53454 | 150 | MPa |
| Split load | DIN 53463 | 2500 | N |
| Modulus of elasticity - bending test | DIN 53457 | 7000 | MPa |
| Resistance between plugs | -- | - | — |
| after 24 h storage in water / 23º C | DIN 53482 | 107 | Ohm |
| 1-minute test voltage | -- | - | — |
| parallel to lamination 8) | DIN 53481 | 20 | kV |
| 1-minute test voltage | -- | - | — |
| perpendicular to lamintion 8) | DIN 53481 | 5 | kV |
| Dielectric loss factor tan d | -- | - | — |
| -50 Hz 96 h 105º C | DIN 53483 | - | max. |
| - 1 MHz 24 h storage in water | DIN 53483 | - | max. |
| Dielectric constant er | DIN 53483 | 5 | >> |
| Tracking resistance index 6) | IEC 112 | 100 | CTI |
| Electrolytic corrosion | DIN 53489 | - | max. |
| Arc resistance | DIN 53484 | - | class |
| Thermal conductivity | DIN 52612 | 0,2 | W/mk |
| Linear expansion coefficient | VDEO3O4/2 | 20-40 | 10-6 /K |
| Temperature Index 4) | VDE 0304/2 | 110 | C |
| Limit value determin. of the limit temp. | -- | - | Limit value determin. of the limit temp. |
| based on flexural str. S bB | -- | 60 | MPa |
| Flammability | UL 94 | - | class |
| Oxygen index | ISO 4589 | - | % |
| Insulating class | IEC PubI.85 | A | E |
| Glow rod test | DIN 53459 | 2b | Stufe |
| Water absorbtion, 4mm thickness 9) | D1N53495 | 120 | mg |
| Colour | -- | brow | — |
| Colour | -- | -- | — |
| Colour | -- | -- | — |